Teknolac Combi 2144-08 Base

Gloss (60°) Maximum 80

TEKNOLAC COMBI 2144-08 is manufactured on the basis of modified alkyd and contains active corrosion pigments.

Area of ​​application Machines

Recommended substrate Steel

Used as a 1-layer varnish on sandblasted substrates (SA 2½) or in combination with TEKNOLAC PRIMER to build up corrosion classes.

Quick drying. Provides a hard surface that is resistant to weak acids and bases as well as oil and water. Suitable for painting machines, racks and steel structures.

Thinner

Standard thinner: TEKNOSOLV 6120-00.

Slow thinner: TEKNOSOLV 6670-00.

Method of application

Airless spraying, Conventional spraying

Pretreatment

The surfaces are cleaned of impurities that can be harmful for pretreatment and application. In addition, water-soluble salts are removed by suitable methods. The surfaces of the various materials are pre-treated as follows:

COLD ROLLED SURFACES: Clean with a suitable pre-treatment chemical.

HOT ROLLED SURFACES: Sandblasted to degree of cleanliness SA 2½ (ISO 8501-1)

Application conditions

The surface to be treated must be dry. During application and drying, the temperature of the air, the surface and the product must be above +5 °C and the relative humidity below 80%. Is normally unlimited overspray proof when diluted with TEKNOSOLV 6670-00. Please ask our consultant for further information.

Drying time +23 °C / 50 % RH (dry film 40 µm)

- duster Approx. 10 minutes (ISO 1517)

- non-stick Approx. 30 minutes (ISO 3678)

- forced drying +60 °C / 50 % RH

- dry thoroughly: 30 min.

With layer thicknesses of 80 µm or more, there is a risk of cracking - if the drying time and temperature are not observed.