20-610-10 2K Pu Nass in Nass Füller 6:1 Creamwhite

The filler is also characterized by its fantastic adhesion and corrosion protection. The primer can be applied directly to small cuts for aluminium.

Particularly good adhesion to sandblasted iron, stainless steel, galvanization and to old prepared lacquers.

Mix ratio Vol. 6:1 Airless / Airmix, 6:1:1 Air/Upper cup/membrane

Hardener 30-699-5 Füllerhärter für 6:1 PU Füller

Thinner SWIN-Universalverdünnung

Spray wipe. v/ 20 °C 25-30 s 4 mm DIN / Airless 40-60 s

Processing

Air / Upper cup = Spray pressure (3-5 bar) Spray nozzle (1.5 mm) Spray passages (2-3)

Airless / Airmix = Spray pressure (approx. 100 bar) Spray nozzle (9-11, 20-60°) Spray paths (2-3)

Potlife 2-5 Hours

Layer thickness / Dry film approx. 60 - 100 µm depending on corrosion category

Deaeration time 20 °C 10-20 min between spray passes, depending on layer thickness

Drying time 20 °C

overpainting/dust dry/handling/assembly

As Nass-in-Nass Filler, overcoatable after 30-40 min. Can be sanded after approx. 4-6 t depending on temperature and layer thickness

Overpainting with SWIN-2 layers-Basislack Silber within the first 3 hours, or after complete drying. Base coat must be set with Universal thinner normal 60-101-6.

For drying times up to 72 hrs. top coat can be applied directly, with a longer drying time an additional layer (20-30 my) is required as an adhesion agent of this Grundierfiller 20-6**-10.

Etch Primer must only be overcoated after (1 hour at 20°) or completely through drying approx. 16 hours. w/20 gr

A direct application on Aluminum is only possible after thorough pre-treatment with SWIN SZ-820-BE Degreaser and pickling agent.

Polyester materials can only be applied after complete drying. The laser covering power has no influence on layer thickness and corrosion properties.